Web Catalogue update October 2019

SUPERFAST GLUE TECHNICAL DATA SHEET 05 4002 Physical Properties in Liquid State Chemical Base Ethyl Cyanoacrylate Curing System Humidity Colour Transparent Viscosity Brookfield at 25°C 20 min-1, densimeter 2 25 - 60 mPa • s Density (25°C) (DIN 51757) 1.05 • 103 kg/m3 Flash Point (COC) (ISO 2592) > 80°C Steam Pressure at 25°C < 1 mbar Shelf Life 12 months mK Physical Properties when Cured Finally Cured after 12 h Linear co-efficient of thermal expansion α ≈ 100 • 10 -6 1/K Specific Thermal Conductivity λ ≈ 0.3 W Specific Electric Loss Resistance D = 0.2 - 1 • 10 16 Ωcm Di-electric Constant (10 kHz) ≈ 2 - 3.5 Di-electric Disruptive Strength E d = 25 kV/mm Di-electric Loss Value (10 kHz) tan δ < 0.02 Distortion Temperature 165°C Functional Properties when Cured (after curing 24h at 25°C Tensile Strength (DIN 53288) 12 - 25 N/mm 2 Comb. Tension and 12 - 26 N/mm 2 Shear Strength τ (DIN 53283) Temperature Range Gap to be glued - 60°C to + 80°C Recommended 0.05 mm Maximum 0.1 9 mm B B Combined Tension and Shear Strength on Various Materials: (N/mm²) Aluminium, Pickled 12 - 19 PVC > 6 ABS > 6 Phenol resin 5 - 15 PC > 5 Rubber (Buna N) > 10 Neoprene > 10 Relative Strength in % 100 h 500 h 1000 h Engine Oil, MIL-L-46152 at 40°C 100 100 95 Petrol at 22°C 100 100 100 Isopropanole at 22°C 100 100 100 1.1.1 Trichlorethane at 22°C 100 100 100 Freon TA at 22°C 100 100 100 NZ. pub. 10/14 ©